Electrode Size
Average Thickness Maximum Recommended
of Material Electrode Diameter
1.0 - 2.0mm 2.5mm
  
5.0 - 8.0mm 4.0mm
8.0 - > mm 5.0mm
The size of the electrode generally depends on the
thickness of the section being welded, and the thicker
the section the larger the electrode required. The table
gives the maximum size of electrodes that maybe used
for various thicknesses of section baseed on using a

Correct current selection for a particular job is an im-
portant factor in arc welding. With the current set too

a stable arc. The electrode tends to stick to the work,
penetration is poor and beads with a distinct rounded
-
nied by overheating of the electrode resulting undercut
and burning through of the base metal and producing
excessive spatter. Normal current for a particular job may be considered as the maximum, which can be
used without burning through the work, over-heating the electrode or producing a rough spattered surface.

Arc Length
To strike the arc, the electrode should be gently scraped on the work until the arc is established. There is a

-
sively short arc will cause sticking of the electrode and result in poor quality welds. General rule of thumb
for down hand welding is to have an arc length no greater than the diameter of the core wire.
Electrode Angle
The angle that the electrode makes with the work is important to ensure a smooth, even transfer of metal.

and 15 degrees towards the direction of travel. When vertical up welding the angle of the electrode should
be between 80 and 90 degrees to the work piece.
Travel Speed
The electrode should be moved along in the direction of the joint being welded at a speed that will give the
size of run required. At the same time, the electrode is fed downwards to keep the correct arc length at all
times. Excessive travel speeds lead to poor fusion, lack of penetration etc, while too slow a rate of travel
will frequently lead to arc instability,slag inclusions and poor mechanical properties.
Material and Joint Preparation
The material to be welded should be clean and free of any moisture, paint, oil, grease, mill scale, rust or
any other material that will hinder the arc and contaminate the weld material. Joint preparation will depend

edges should be clean and free of any contaminates. The type of joint will be determined by the chosen
application.
Welding Current (Amperage)
Electrode Size Current Range
ø mm (Amps)
2.5mm 60 - 100
  
  
5.0mm 165 - 260
Electrode Selection
As a general rule, the selection of an electrode is straight forward,in that it is only a matter of selecting an
electrode of similar composition to the parent metal. However, for some metals there is a choice of several

consult your welding supplier for the correct selection of electrode.